ABSTRACT
In this work, the effect of various heat treatments on ST 60Mn steel on its fatigue strength prior to use and after use was studied it was observed that by normalising for service conditions not exceeding 10 stress cycle, the fatigue strength was raised by a factor of 1 2.
Oluwole, O (2021). EFFECT OF HEAT TREATMENT ON THE DAMAGE RATIO OF CORRODED ST 60. MN STEEL. Afribary. Retrieved from https://track.afribary.com/works/effect-of-heat-treatment-on-the-damage-ratio-of-corroded-st-60-mn-steel
Oluwole, O "EFFECT OF HEAT TREATMENT ON THE DAMAGE RATIO OF CORRODED ST 60. MN STEEL" Afribary. Afribary, 24 Mar. 2021, https://track.afribary.com/works/effect-of-heat-treatment-on-the-damage-ratio-of-corroded-st-60-mn-steel. Accessed 25 Dec. 2024.
Oluwole, O . "EFFECT OF HEAT TREATMENT ON THE DAMAGE RATIO OF CORRODED ST 60. MN STEEL". Afribary, Afribary, 24 Mar. 2021. Web. 25 Dec. 2024. < https://track.afribary.com/works/effect-of-heat-treatment-on-the-damage-ratio-of-corroded-st-60-mn-steel >.
Oluwole, O . "EFFECT OF HEAT TREATMENT ON THE DAMAGE RATIO OF CORRODED ST 60. MN STEEL" Afribary (2021). Accessed December 25, 2024. https://track.afribary.com/works/effect-of-heat-treatment-on-the-damage-ratio-of-corroded-st-60-mn-steel